Scientific Reports volume 12, Article number: 10045 (2022) Cite this article

1761 Accesses

4 Citations

2 Altmetric

Metrics details

Highly crystalline Bi2Te3 based compounds with small grain size were successfully synthesized by flash sintering (FS) method in 10 s at room temperature under suitable current density using Bi, Te and Se powders. The instantaneously generated local Joule heat at grain boundary is regarded as the main reason for the rapid completion of chemical reaction and crystallization. By combining FS synthesis method with spark plasma sintering (SPS), Bi2Te3 based bulk materials with high relative density were fabricated in 10 min. Suitably prolonging sintering temperature and holding time in SPS process can decrease carrier concentration and phonon thermal conductivity, while increasing carrier mobility. Hence, the sample prepared at 753 K for 3 min shows 20% higher ZT value than that of the sample prepared at 723 K for 3 min. Compared with common zone melting or powder metallurgy methods taking several hours by complex operation, this method is time-saving and low cost.

With the increasingly serious energy and environmental crisis, exploring clean energy resources and green energy conversion technologies become urgent and mandatory for the researchers in related fields1. Thermoelectric material is a kind of functional material which can realize the direct conversion between heat and electricity by Seebeck effect and Peltier effect2. Because of its pure solid state operation mode, high stability and long life, thermoelectric technology provides opportunities to harvest useful electricity from waste heat or to realize in situ refrigeration3,4,5. The conversion performance of thermoelectric material is usually evaluated by the dimensionless figure of merit ZT, which can be expressed as ZT = S2σT/κ, where S is the Seebeck coefficient, σ is the electrical conductivity, κ is the thermal conductivity (including electronic thermal conductivity κe, lattice thermal conductivity κl and bipolar thermal conductivity κb) and T is the absolute temperature6. Therefore, high electrical conductivity, large Seebeck coefficient and low thermal conductivity should be simultaneously owned for an ideal thermoelectric material7. Bismuth telluride (Bi2Te3) is a kind of narrow band gap semiconductor material, which has relatively high electrical conductivity, large Seebeck coefficient and low thermal conductivity between 300–500 K8. Up to now, bismuth telluride and its alloys with antimony telluride or bismuth selenide have been the most mature thermoelectric material systems to be used at near room temperature9,10. Some commercial thermoelectric devices and modules for power generation and solid-state cooling at this temperature range have been successfully developed based on bismuth telluride and its alloys11.

Nowadays, commercial bismuth telluride based thermoelectric materials are generally produced by zone melting (ZM) method. Although ZM technique is convenient, its fabrication process is rather time consuming and energy intensive12. The prolonged annealing at high temperature may also lead to composition deviation, thus deteriorating thermoelectric performance. Moreover, the fabricated products are highly oriented and can cleave easily along the basal plane, thereby resulting in poor mechanical properties and limiting long-term usage13. Therefore, powder metallurgy techniques combining with advanced sintering techniques were explored extensively in recent years to fabricate polycrystalline bismuth telluride based thermoelectric materials with both high mechanical and thermoelectric properties. For example, high energy ball milling, melt spinning and various wet chemical methods have been successfully developed to synthesize Bi2Te3 based compounds with small grain size and modulated microstructure14,15,16,17. By combining these synthesis methods with hot pressing (HP) or spark plasma sintering (SPS) techniques, relatively robust mechanical properties and high thermoelectric performance have been simultaneously achieved in bismuth telluride based bulk materials. However, these synthesis methods are still time consuming and energy intensive, and the products may be oxidized or polluted by medium and organic impurities in the synthetic process, resulting in deteriorated thermoelectric performance18. Therefore, it is of great interest to develop new fabrication methods for high performance polycrystalline bismuth telluride based thermoelectric materials with low cost, high efficiency and simple craft process.

Over the past 10 years, flash sintering (FS) has been demonstrated as a novel technique to fabricate ceramic materials. Under the combined action of external electric field and thermal field, the sintering densification of ceramics can be achieved at low temperature within a few seconds19,20,21. Therefore, flash sintering is much more cost-effective and energy-efficient than traditional high temperature sintering method taking several hours. Recently, this technique has been successfully extended to reactive FS, which can induce both phase transformation and sintering densification. For example, dense Na0.5K0.5NbO3 ceramics have been reported to be fabricated with NaNbO3 and KNbO3 mixed powders by reactive FS, in which the chemical reaction and sintering occur simultaneously22. This rapid preparation method at low temperature can effectively reduce the loss of volatile elements and restrain grain growth, which are beneficial for the enhancement of thermoelectric performance. Therefore, flash sintering shows tremendous potential in the fabrication of high-performance thermoelectric materials. However, up to now there are few papers related to the FS of thermoelectric materials. The preparations of thermoelectric materials are generally realized by a flash derivative that is called flash-SPS, which uses SPS equipment to produce rapid heating rate similar to FS23,24,25. In the process of flash-SPS, no mold is used so that current passes directly through the cold pressed or pre-densified sample held directly between graphite punches. Actually, flash-SPS is used as a rapid sintering method for the densification of bulk thermoelectric materials with pre-synthesized compounds as raw materials26,27,28,29. For example, the fabrications of highly dense Sb2Te3 bulk materials were conducted by flash-SPS with a current feed duration of 1 s using commercial Sb2Te3 raw powder29. However, nearly no literature has been reported for the synthesis of thermoelectric compounds by FS.

In this work, we demonstrate that Bi2Te3 based compounds can be synthesized efficiently by FS method through adjusting suitable current density. The results indicate that highly crystalline Bi2Te3 based compounds with small grain size can be synthesized in 10 s at room temperature using commercial Bi, Te and Se powders with much larger size by an ordinary direct current power supply. By combining FS with SPS, Bi2Te3 based bulk materials with nominal composition and high density can be prepared. Hence, this method is hopeful for the mass production of bismuth telluride based thermoelectric materials.

Schematic diagram of the FS apparatus is shown in Fig. 1. The mixture of Bi and Te raw powders according to the stoichiometric composition of Bi2Te3 was loaded into a graphite mold, the inner wall of which was insulated by a piece of mica paper to ensure that current only passed through the mixture rather than the graphite mold. A thermocouple was inserted into a Φ1.8 mm hole in the middle of the graphite mold to measure the transient surface temperature of the sample. Two pieces of graphite papers were loaded between the sample and the punches for easily taking out of the product. The mixed powder was compacted by the upper and lower punches on a tablet press, and then the pressure was released. Whereafter, direct current with certain density passed through the compacted mixture to realize the FS of Bi2Te3 compound. Generally, tellurium is partially substituted by selenium to optimize the carrier and thermal transport properties of Bi2Te3. Hence, another sample with the stoichiometric composition of Bi2Te2.7Se0.3 was also synthesized using Bi, Te and Se powders by FS. The synthesized Bi2Te3−xSex compounds by FS were then ground to powders for SPS.

Schematic diagram of the FS apparatus.

XRD patterns of the Bi2Te3 compound synthesized by FS and the Bi2Te3−xSex bulk samples further prepared by SPS on different conditions are shown in Fig. 2. For the Bi2Te3 compound synthesized by FS, all diffraction peaks are well indexed to the standard JCPDS card (PDF#15-0863) of Bi2Te3 with rhombohedral crystal structure and no peak related to oxidation or impurity can be detected, indicating that single phase Bi2Te3 compound with high crystallinity can be synthesized by FS in 10 s at room temperature using Bi and Te powders. As illustrated in Table. 1, the compound synthesized by FS has well matched composition to the desired stoichiometry of Bi2Te3 as measured by ICPOES, indicating that no volatilization of Te occurred in the process of FS. The transient surface temperature of the sample synthesized by FS was measured to be 625 K when current passed through the sample for 1 s, meaning that an order of 104 K/min self-heating rate of the specimen had been achieved. This extremely rapid Joule heating occurring on the macroscale is considered to be attributed to the heat localization at grain boundary, which may result in the instantaneous occurrences of chemical reaction and crystallization30. In the experiment, we found that there is a threshold value of current density for the synthesis of Bi2Te3 compound by FS, which is about 8 A/cm2. Below the current density of 8 A/cm2, FS does not happen because of the deficient Joule heat. Furthermore, volume expansion of the sample was observed after FS. Considering the transient surface temperature of the sample in FS process is much higher than the melting point of Bi (544.6 K), the synthetic process should include the melting of Bi and subsequent chemical reaction with Te to form Bi2Te3 based compounds. Because of the volume expansion after FS, the relative density of the product is only about 70.4% calculated by the theoretical density 7.73 g cm−3. The Bi2Te3 based compounds synthesized by FS were then ground to powder and sintered further to compact pellets by SPS on different conditions. The main peaks of the Bi2Te3−xSex bulk samples further prepared by SPS on different conditions are also well in accordance with the standard JCPDS card (PDF#15-0863) of Bi2Te3. After SPS, the samples show higher relative intensity of (00 l) peaks, indicating the enhanced preferential orientation of basal (00 l) planes perpendicular to the pressing direction. To investigate the degree of preferred orientation of (00 l) planes, orientation factors F were calculated using Lotgering method, which can be expressed by the following formulae:

where I(hkl) and I0(hkl) are the peak integral intensities for the measured and randomly oriented samples, respectively31,32. The orientation degree was enhanced with the increase of sintering temperature and holding time in SPS process, as indicated in Table. 1. However, the highest value of F obtained for the sample sintered at 753 K for 3 min is only about 0.095, which indicates that almost no highly oriented textures in the samples were formed in SPS process although bismuth telluride tends to grow along the ab plane. As shown in Table 1, the Bi2Te3−xSex bulk samples further prepared by SPS on different conditions all show relative densities higher than 98.5%. However, the compositions deviate a little to the lack of tellurium and selenium, as measured by ICPOES.

XRD patterns of the Bi2Te3 compound synthesized by FS and the Bi2Te3−xSex bulk samples further prepared by SPS on different conditions.

The SEM images of Bi, Te and Se raw powders are shown in Fig. 3a–c, which have powder size of about 10–30 μm. For comparison, the Bi2Te3 and Bi2Te2.7Se0.3 compounds synthesized by FS have high crystallinity and compactness, as shown in Fig. 3d and e. Moreover, the size of the generated crystalline grain declines to about 1–3 μm, indicating that polycrystalline Bi2Te3 compound with much smaller grain size can be synthesized with micron Bi, Te and Se powders by FS. Thus, it shows great promise to synthesize Bi2Te3 based compounds with nanocrystalline by using nanoscale raw powders. The fracture morphologies of the Bi2Te3 based bulk materials subsequently prepared by SPS on different conditions are shown in Fig. 3f–i. The Bi2Te3 bulk samples prepared by SPS on different conditions are all highly dense with the typical layered structure. With the increase of sintering temperature and holding time in SPS process, it can be seen that the grain size becomes more homogeneous and the amount of nano cavity decreases because of more sufficient element diffusion and grain growth. Compared with the sample synthesized by FS, grain size increases to about 3–8 μm after SPS process. The grain structures of the Bi2Te3 bulk samples prepared by SPS on different conditions show no obvious preferred orientation, which are consistent with the results of XRD. The energy dispersive X-ray spectroscopy (EDS) patterns illustrate that the products only contain Bi, Te and Se elements, as shown in the insets in Fig. 3f–i. Due to the high-efficiency, low energy consumption and convenient operation process, FS combining with SPS can be considered as a promising method for the large-scale fabrication of Bi2Te3 based polycrystalline thermoelectric materials.

SEM images of (a) Bi, (b) Te and (c) Se raw powders. Cross-section SEM images of (d) Bi2Te3 compound synthesized by FS, (e) Bi2Te2.7Se0.3 compound synthesized by FS, (f) Bi2Te3 sample further prepared by SPS at 723 K for 3 min, (g) Bi2Te3 sample further prepared by SPS at 753 K for 2 min, (h) Bi2Te3 sample further prepared by SPS at 753 K for 3 min, (i) Bi2Te2.7Se0.3 sample further prepared by SPS at 753 K for 3 min. The insets show the EDS patterns.

To validate the effects of sintering temperature and holding time in SPS process on electrical transport properties of the samples, numerical values for carrier concentration (n) and mobility (μ) derived from Hall effect measurements at 313 K perpendicular to the SPS pressing direction are shown in Fig. 4a. All samples have negative values of carrier concentration, manifesting the dominance of electron in the transport process. With the increase of sintering temperature and holding time, carrier concentration decreases and carrier mobility increases. When sintering temperature and holding time increase, more power is supplied to the sample, which would lead to the volatilization of Te, as evidenced by the composition analysis in Table 1. Bi atom will enter into the Te vacancy because of the small difference in electronegativity between Bi and Te and more antisite defect BiTe will be produced. That means more hole could be generated to neutralize electron in these n-type samples, resulting in decreased carrier concentration. Absolute values of carrier concentration are around 8 × 1019–9 × 1019/cm3 for these samples, which is more than an order of magnitude higher than that of conventional zone melted sample33. Generally, the ion defects generated in sample under high electric field are tend to ionize to electron and uncharged lattice defect34. Therefore, the large carrier concentration probably arises from the effect of electric field in FS process. Compared with Bi2Te3 samples, Bi2Te2.7Se0.3 sample shows lower carrier concentration. For n-type Bi2Te3 based compounds, antisite defect TeBi is the dominant point defect which determines the carrier concentration. Although the equivalent dopant of Se is neutral, it may affect the formation of intrinsic point defect TeBi and thus the carrier concentration35,36,37. On the other hand, carrier mobility increases obviously from about 118 cm2/V s to 141 cm2/V s when the sintering temperature increases from 723 to 753 K for 3 min. The higher carrier mobility should be brought by the increased crystallinity of the product and the further eliminated microstructure defect at higher sintering temperature and longer holding time. After selenium doping, the carrier mobility decreases to 115 cm2/V s mainly due to the enhanced alloy scattering.

Electrical transport properties of the bulk Bi2Te3−xSex samples prepared by SPS on different conditions. (a) Carrier concentration n and mobility μ at 313 K, (b–d) Temperature dependence of electrical conductivity σ, Seebeck coefficient S and power factor PF.

Thermoelectric properties of the bulk Bi2Te3−xSex samples prepared by SPS on different conditions were measured along the direction perpendicular to the SPS pressing direction. Figure 4b presents the change of electrical conductivity with measuring temperature. In whole measuring temperature range, the electrical conductivities decrease monotonically with the increasing measuring temperature for all samples, indicating a degenerate semiconductor feature. With the increase of sintering temperature and holding time in SPS process, the electrical conductivity increases slightly. Electrical conductivity σ is determined by carrier concentration and mobility as described by the relationship σ = neμ, where n is carrier concentration, μ is carrier mobility, and e is the electronic charge. Although carrier concentration decreases with the increase of sintering temperature and holding time because of the increased volatilization of Te and the resulted more antisite defect BiTe, carrier mobility is obviously elevated due to more sufficient element diffusion and grain growth, as evidenced in Fig. 4a. Therefore, the enhanced carrier mobility counteracts the effect of decreased carrier concentration and results in a higher electrical conductivity. The electrical conductivity at room temperature of the sample prepared at 753 K for 3 min is approximate 1800 S/cm, which is even higher than that of the specimen prepared by hot pressing followed with hot deformation38. Because carrier concentration and mobility both decrease after partial substitution of selenium for tellurium due to the reduction of the number of intrinsic point defect TeBi and enhancement of alloy scattering as discussed above, Bi2Te2.7Se0.3 sample shows lower electrical conductivity than Bi2Te3 samples.

Figure 4c shows the temperature dependence of Seebeck coefficient for the bulk Bi2Te3−xSex samples prepared by SPS on different conditions. Seebeck coeffcients of the samples all exhibit negative values over the entire measuring temperature range, indicating as n-type semiconductors, which is consistent with the results of Hall effect measurements. With the increasing sintering temperature and holding time in SPS process, the absolute value of Seebeck coeffcient increases evidently. The Seebeck coeffcient of Bi2Te3 prepared at 723 K for 3 min is about – 132 μV/K at 473 K and the value is promoted to – 142 μV/K at 473 K for the sample prepared at 753 K for 3 min. According to Boltzmann transport theory, Seebeck coeffcient is inversely proportional to carrier concentration for solid thermoelectric materials. Therefore, the enhanced Seebeck coeffcient is mainly due to the decreased carrier concentration, as shown in Fig. 4a. Furthermore, the Bi2Te2.7Se0.3 sample shows much higher Seebeck coeffcients than Bi2Te3 samples. The promoted Seebeck coeffcient is also due to the lower carrier concentration after partial substitution of selenium and the resulted reduction of intrinsic point defect TeBi. Seebeck coeffcients of the samples increase with increasing measuring temperature to about 480 K and then decrease slowly, showing a distinct temperature dependence from zone melted sample which shows monotonical downtrend39. The increase of Seebeck coeffcient in a wide temperature range is beneficial for the sustainability of high power factor.

Figure 4d shows the temperature dependence of power factor for the bulk Bi2Te3−xSex samples prepared by SPS on different conditions, which is calculated from electrical conductivity and Seebeck coefficient. With the increase of sintering temperature and holding time in SPS process, power factor is much enhanced owing to the increase in electrical conductivity and Seebeck coeffcient. Power factor of the sample prepared at 753 K for 3 min reaches to 2.5 mW/m K2 at 353 K, almost being 16% improvement compared with the sample prepared at 723 K for 2 min. Due to the high electrical conductivity and modest Seebeck coefficient of the sample, this value of power factor is even higher than that of the sample prepared by high-energy ball milling combining with SPS using commercial Bi and Te powders40. Furthermore, the value of power factor remains above 1.7 mW/m K2 in the whole measuring temperature range of 200 K, showing good stability with temperature. Although electrical conductivity decreases after partial substitution of selenium for tellurium, Bi2Te2.7Se0.3 shows even higher power factor than Bi2Te3 due to the enhanced Seebeck coefficient.

The temperature dependence of thermal conductivity for the bulk Bi2Te3−xSex samples prepared by SPS on different conditions is shown in Fig. 5. The total thermal conductivity κ as illustrated in Fig. 5a decreases with increasing sintering temperature in SPS process over the entire measuring temperature range. However, with the increase of holding time, the thermal conductivity increases. Therefore, the sample prepared at 753 K for 2 min shows the lowest value of thermal conductivity. The electronic thermal conductivity κe can be estimated by the Wiedemann−Franz law κe = LσT, where L is the Lorentz number, σ is the measured electrical conductivity, and T is the absolute temperature. Based on the single parabolic band (SPB) model under relaxation time approximation, temperature dependent Lorenz number L can be calculated by the following equations:

where kB is the Boltzmann constant, e is the electron charge, λ is the scattering parameter (λ = − 1/2 for acoustic phonon scattering) and η is the reduced Fermi energy8. The determination of η is based on the measured Seebeck coefficient S, which is expressed as

Thermal transport properties of the bulk Bi2Te3−xSex samples prepared by SPS on different conditions. Temperature dependence of (a) total thermal conductivity κ, (b) Lorentz number L, (c) electronic thermal conductivity κe and (d) lattice thermal conductivity κl plus bipolar thermal conductivity κb.

As shown in Fig. 5c, the electronic thermal conductivities κe decrease monotonically with the increasing measuring temperature for all samples, which show the same trend as that of electrical conductivity. The temperature dependence of κl + κb is illustrated in Fig. 5d. Compared with the value of κe, κl + κb has larger contribution to the total thermal conductivity for Bi2Te3 samples. Because Seebeck coefficients all have the maximum value at around 480 K as discussed above, the intrinsic excitation should not occur below 400 K for all samples. That means bipolar thermal conductivity κb can be ignored and lattice thermal conductivity κl occupies the largest part of total thermal conductivity below 400 K. Although carrier concentrations and electrical conductivites are relatively high for these Bi2Te3 samples, phonon is still the predominant carrier for heat transport below 400 K. It is worth noting that κe and κl + κb are both decreased by partially substituting selenium for tellurium. Especially, the lattice thermal conductivity κl is lower than the electronic thermal conductivity κe for Bi2Te2.7Se0.3 below 400 K, indicating that phonon can been scattered greatly by alloying selenium due to the mass and size difference between Te and Se. As the Debye temperature of Bi2Te3−xSex is as low as 156 K, the main mechanism of phonon scattering is based on Umklapp process at near room temperature and lattice thermal conductivity κl would be inversely related to temperature. The total thermal conductivities all decrease and then increase with the increase of measuring temperature, as shown in Fig. 5a. Because electronic and lattice thermal conductivities both decrease monotonically with the increasing measuring temperature, bipolar thermal conductivity becomes a major contributor to the total thermal conductivity at high temperature.

Figure 6 shows the temperature dependence of dimensionless figure of merit (ZT) for the bulk Bi2Te3−xSex samples prepared by SPS on different conditions. ZT values of the Bi2Te3 samples increase with temperature initially and then decrease at around 430 K. As dicussed above, the enhancement of power factor and suppression of thermal conductivity have been realized simultaneously by properly increasing the sintering temperature and holding time in SPS process. Therefore, the Bi2Te3 sample prepared at 753 K for 3 min shows 20% higher ZT value than that of the sample prepared at 723 K for 3 min. After partial substitution of selenium for tellurium, Bi2Te2.7Se0.3 shows a ZT value of 0.71 at 393 K. Although smaller than that of state-of-the-art, this value is actually comparable to those obtained in Bi2Te3 based nanocomposite bulk materials prepared by SPS and some other reference data41,42,43,44.

Temperature dependence of ZT values of the bulk Bi2Te3−xSex samples prepared by SPS on different conditions.

In summary, FS method has been successfully employed to synthesize highly crystalline Bi2Te3 based compounds with small grain size in 10 s at room temperature using commercial Bi, Te and Se powders with much larger size. The instantaneously generated local Joule heat at grain boundary by passing current through sample is regarded as the main cause for the rapid completion of chemical reaction and crystallization. This rapid synthesis method at room temperature can significantly restrain grain growth and avoid tellurium volatilization. By combining FS synthesis method with SPS technique, Bi2Te3 based bulk materials with high relative density and thermoelectric performance can be fabricated in 10 min. Compared with common zone melting or powder metallurgy methods taking several hours by complex operation, this method is time-saving and low cost. In SPS process, the enhancement of electrical transport property and suppression of thermal transport property can be simultaneously obtained by suitably prolonging sintering temperature and holding time. Compared with the sample prepared at 723 K for 3 min, the sample prepared at 753 K for 3 min shows 20% higher ZT value. The results demonstrate that FS combining with SPS is a promising method to prepare bismuth telluride based thermoelectric materials efficiently and economically.

Commercial Bi (99.99%, Macklin Inc.), Te (99.99%, Macklin Inc.) and Se (99.99%, Macklin Inc.) powders under 200 mesh were used for synthesis without any further purification. The raw powders were weighed according to the stoichiometric composition of Bi2Te3−xSex and then ground uniformly in an agate mortar. The mixture was loaded into a Φ13.2 mm graphite mold, the inner wall of which was insulated by a piece of mica paper to ensure that current only passed through the mixture rather than the graphite mold. Two Φ12.8 mm stainless-steel punches were used to press the mixed powder under 1.5 MPa by tablet press. Then the pressure was released, and the upper and lower punches were connected to a direct current power supply (PPS 2416, Lanyi, China). Voltage of 10 V and current limit of 32.15 A were preset. The sample was maintained at the current limit for 10 s at room temperature, before the power supply was turned off. The obtained product was further ground to powder and then sintered to compact bulk materials under a pressure of 40 MPa at 723 ~ 753 K for 2 ~ 3 min by SPS. The heating rate was set to be 80 K/min and the vacuum degree of cavity was under 6 Pa in SPS process. The obtained disk-shaped samples with diameter of 12.8 mm and height of 11.5 mm were cut along the direction perpendicular to the pressuring direction for thermoelectric performance measurement.

Phase compositions and crystallographic structures of the samples were identified by X-ray diffraction (XRD, Rigaku D/MAX 2200 PC) measurements using Cu Kα radiation (λ = 0.154056 nm). Morphologies and compositions of the raw powders and prepared products were investigated by field emission scanning electronic microscopy (FE-SEM, FEI Sirion 200) equiped with energy-dispersive spectroscope (EDS). Accurate elemental content analyses were carried out on a inductively coupled plasma optical emission spectrometer (ICPOES, Agilent ICPOES730). Electrical conductivities (σ) and Seebeck coefficients (S) were simultaneously measured using a commercial instrument (Cryoall CTA-3S) under a helium atmosphere. Hall coefficients (RH) were measured at near room temperature by van der Pauw method on a commercial Hall effect measurement system (Nanometrics HL5500PC). The values of carrier concentrations (n) were calculated via n = 1/(eRH) and the in-plane carrier mobilities (μ) were obtained through μ = σRH. The values of thermal conductivitie (κ) were calculated according to the relation κ = DCpρ, where the thermal diffusivities (D) were determined by the laser flash method (Netzsch LFA475), specific heats (Cp) were measured on a differential scanning calorimeter (TA DSC25), and mass densities (ρ) were determined by the method of Archimedes. To eliminate the effect of preference orientation on thermoelectric properties, the measuring of electrical and thermal properties are both along the direction perpendicular to the SPS pressing direction.

The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.

Zhang, Q. et al. Emerging technologies for green energy conversion and storage. Adv. Sustain. Syst. 5, 2000152 (2021).

Article Google Scholar

Shi, X. L., Zou, J. & Chen, Z. G. Advanced thermoelectric design: From materials and structures to devices. Chem. Rev. 120, 7399–7515 (2020).

Article CAS PubMed Google Scholar

Pourkiaei, S. M. et al. Thermoelectric cooler and thermoelectric generator devices: A review of present and potential applications, modeling and materials. Energy 186, 115849 (2019).

Article Google Scholar

Russ, B., Glaudell, A., Urban, J. J., Chabinyc, M. L. & Segalman, R. A. Organic thermoelectric materials for energy harvesting and temperature control. Nat. Rev. Mater. 1, 1–14 (2016).

Article CAS Google Scholar

Mao, J., Chen, G. & Ren, Z. Thermoelectric cooling materials. Nat. Mater. 20, 454–461 (2021).

Article ADS CAS PubMed Google Scholar

Ioffe, A. F. Semiconductor Thermoelements and Thermoelectric Cooling (Infosearch, 1957).

Google Scholar

Snyder, G. J. & Toberer, E. S. Complex thermoelectric materials. Nat. Mater. 7, 105–114 (2008).

Article ADS CAS PubMed Google Scholar

Zhu, B. et al. Realizing record high performance in n-type Bi2Te3-based thermoelectric materials. Energy Environ. Sci. 13, 2106–2114 (2020).

Article CAS Google Scholar

Pei, J., Cai, B., Zhuang, H. L. & Li, J. F. Bi2Te3-based applied thermoelectric materials: Research advances and new challenges. Natl. Sci. Rev. 7, 1856–1858 (2020).

Article PubMed PubMed Central Google Scholar

Tan, G., Ohta, M. & Kanatzidis, M. G. Thermoelectric power generation: From new materials to devices. Philos. Trans. R. Soc. A 377, 20180450 (2019).

Article ADS CAS Google Scholar

Chen, Y., Hou, X., Ma, C., Dou, Y. & Wu, W. Review of development status of Bi2Te3-based semiconductor thermoelectric power generation. Adv. Mater. Sci. Eng. 1, 1210562 (2018).

Google Scholar

Zheng, G. et al. High thermoelectric performance of p-BiSbTe compounds prepared by ultra-fast thermally induced reaction. Energy Environ. Sci. 10, 2638–2652 (2017).

Article CAS Google Scholar

Zheng, Y. et al. High-temperature mechanical and thermoelectric properties of p-type Bi0.5Sb1.5Te3 commercial zone melting ingots. J. Electron. Mater. 43, 2017–2022 (2014).

Article ADS CAS Google Scholar

Zhuang, H. L. et al. Thermoelectric performance enhancement in BiSbTe alloy by microstructure modulation via cyclic spark plasma sintering with liquid phase. Adv. Funct. Mater. 31, 2009681 (2021).

Article CAS Google Scholar

Ge, Z. H. et al. Enhanced thermoelectric properties of bismuth telluride bulk achieved by telluride-spilling during the spark plasma sintering process. Scr. Mater. 143, 90–93 (2018).

Article CAS Google Scholar

Deng, R. et al. High thermoelectric performance in Bi0.46Sb1.54Te3 nanostructured with ZnTe. Energy Environ. Sci. 11, 1520–1535 (2018).

Article CAS Google Scholar

Mamur, H., Bhuiyan, M. R. A., Korkmaz, F. & Nil, M. A review on bismuth telluride (Bi2Te3) nanostructure for thermoelectric applications. Renew. Sust. Energ. Rev. 82, 4159–4169 (2018).

Article CAS Google Scholar

Hong, M., Chen, Z. G. & Zou, J. Fundamental and progress of Bi2Te3-based thermoelectric materials. Chin. Phys. B 27, 048403 (2018).

Article ADS CAS Google Scholar

Yu, M., Grasso, S., Mckinnon, R., Saunders, T. & Reece, M. J. Review of flash sintering: materials, mechanisms and modelling. Adv. Appl. Ceram. 116, 24–60 (2017).

Article CAS Google Scholar

Biesuz, M. & Sglavo, V. M. Flash sintering of ceramics. J. Eur. Ceram. Soc. 39, 115–143 (2019).

Article CAS Google Scholar

Becker, M. Z., Shomrat, N. & Tsur, Y. Recent advances in mechanism research and methods for electric-field-assisted sintering of ceramics. Adv. Mater. 30, 1706369 (2018).

Article CAS Google Scholar

Wu, Y., Su, X., An, G. & Hong, W. Dense Na0.5K0.5NbO3 ceramics produced by reactive flash sintering of NaNbO3-KNbO3 mixed powders. Scr. Mater. 174, 49–52 (2020).

Article CAS Google Scholar

Gucci, F., Saunders, T. G. & Reece, M. J. In-situ synthesis of n-type unfilled skutterudite with reduced thermal conductivity by hybrid flash-spark plasma sintering. Scr. Mater. 157, 58–61 (2018).

Article CAS Google Scholar

Du, B. et al. Flash spark plasma sintering of magnesium silicide stannide with improved thermoelectric properties. J. Mater. Chem. C 5, 1514–1521 (2017).

Article CAS Google Scholar

Yu, M. et al. Magnéli phase titanium suboxides by flash spark plasma sintering. Scr. Mater. 146, 241–245 (2018).

Article CAS Google Scholar

Srinivasan, B. et al. Effect of the processing route on the thermoelectric performance of nanostructured CuPb18SbTe20. Inorg. Chem. 57, 12976–12986 (2018).

Article CAS PubMed Google Scholar

Gucci, F. et al. Hybrid Flash-SPS of TiNiCu0.05Sn with reduced thermal conductivity. J. Alloys Compd. 837, 155058 (2020).

Article CAS Google Scholar

Srinivasan, B. et al. Realizing a stable high thermoelectric zT ∼ 2 over a broad temperature range in Ge1−x−yGaxSbyTe via band engineering and hybrid flash-SPS processing. Inorg. Chem. Front. 6, 63–73 (2019).

Article CAS Google Scholar

Mikami, M. et al. Flash-sintering of antimony telluride and its thermoelectric properties. J. Appl. Phys. 124, 105104 (2018).

Article ADS CAS Google Scholar

Zhou, H. et al. Review of flash sintering with strong electric field. High Voltage 1, 1–11 (2021).

Google Scholar

Lotgering, F. K. Topotactical reactions with ferrimagnetic oxides having hexagonal crystal structures I. J. Inorg. Nucl. Chem. 9, 113–116 (1959).

Article CAS Google Scholar

Shen, J. J. et al. Recrystallization induced in situ nanostructures in bulk bismuth antimony tellurides: A simple top down route and improved thermoelectric properties. Energy Environ. Sci. 3, 1519–1523 (2010).

Article CAS Google Scholar

Zheng, G. et al. High thermoelectric performance of mechanically robust n-type Bi2Te3–xSex prepared by combustion synthesis. J. Mater. Chem. A 3, 6603–6613 (2015).

Article CAS Google Scholar

Narayan, J. A new mechanism for field-assisted processing and flash sintering of materials. Scr. Mater. 69, 107–111 (2013).

Article CAS Google Scholar

Wang, S., Xie, W., Li, H. & Tang, X. Enhanced performances of melt spun Bi2(Te, Se)3 for n-type thermoelectric legs. Intermetallics 19, 1024–1031 (2011).

Article CAS Google Scholar

Hu, L. P., Zhu, T., Liu, X. & Zhao, X. Point defect engineering of high-performance bismuth-telluride-based thermoelectric materials. Adv. Funct. Mater. 24, 5211–5218 (2014).

Article CAS Google Scholar

Zhang, Q. et al. Tuning optimum temperature range of Bi2Te3-based thermoelectric materials by defect engineering. Chem. Asian. J. 15, 2775–2792 (2020).

Article CAS PubMed Google Scholar

Hu, L. P. et al. Improving thermoelectric properties of n-type bismuth–telluride-based alloys by deformation-induced lattice defects and texture enhancement. Acta Mater. 60, 4431–4437 (2012).

Article ADS CAS Google Scholar

Yu, F. et al. Enhanced thermoelectric figure of merit in nanocrystalline Bi2Te3 bulk. J. Appl. Phys. 105, 094303 (2009).

Article ADS CAS Google Scholar

Zhao, L. D., Zhang, B. P., Li, J. F., Zhang, H. L. & Liu, W. S. Enhanced thermoelectric and mechanical properties in textured n-type Bi2Te3 prepared by spark plasma sintering. Solid State Sci. 10, 651–658 (2008).

Article ADS CAS Google Scholar

Raphel, A., Vivekanandhan, P. & Kumaran, S. High entropy phenomena induced low thermal conductivity in BiSbTe1.5Se1.5 thermoelectric alloy through mechanical alloying and spark plasma sintering. Mater. Lett. 269, 127672 (2020).

Article CAS Google Scholar

Chen, X. et al. Enhanced thermoelectric performance of Bi2Te2.7Se0.3/Bi2S3 synthesized by anion exchange method. Phys. Status Solidi RRL 14, 1900679 (2020).

Article CAS Google Scholar

Lee, S. S. et al. Enhanced thermoelectric performance of Mo nanoparticle decorated n-type Bi2Te2.7Se0.3 powder composites. Appl. Surf. Sci. 548, 149200 (2021).

Article CAS Google Scholar

Cho, J. et al. Cu nanoparticle-processed n-type Bi2Te2.7Se0.3 alloys for low-temperature thermoelectric power generation. J. Alloy. Compd. 884, 161060 (2021).

Article CAS Google Scholar

Download references

This work was supported by the National Natural Science Foundation of China (U2006218), the Qin Xin Talents Cultivation Program of Beijing Information Science & Technology University (QXTCP A202103), and the Research Fund Program of Beijing Information Science & Technology University (2021XJJ72, 2021XJJ67).

Beijing Key Laboratory for Sensors, Beijing Information Science & Technology University, Beijing, 100192, China

Zhiwei Zhang, Minna Sun, Mengran Su, Qingwei Liao & Lei Qin

Beijing Key Laboratory for Optoelectronic Measurement Technology, Beijing Information Science & Technology University, Beijing, 100192, China

Zhiwei Zhang, Minna Sun, Lili Cao, Qingwei Liao & Lei Qin

AECC Aero Engine Academy of China, Beijing, 101304, China

Jinchao Liu

Research Institute for Frontier Science, Beihang University, Beijing, 100083, China

Yuan Deng

You can also search for this author in PubMed Google Scholar

Z.W.Z. designed the project, performed part of the experiments and drafted the manuscript. M.R.S. performed part of the experiments; L.L.C., Q.W.L. and L.Q. reviewed the manuscript. M.N.S., J.C.L. and Y.D. added their input in results and discussions.

Correspondence to Lei Qin.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Zhang, Z., Sun, M., Liu, J. et al. Ultra-fast fabrication of Bi2Te3 based thermoelectric materials by flash-sintering at room temperature combining with spark plasma sintering. Sci Rep 12, 10045 (2022). https://doi.org/10.1038/s41598-022-14405-5

Download citation

Received: 01 April 2022

Accepted: 07 June 2022

Published: 16 June 2022

DOI: https://doi.org/10.1038/s41598-022-14405-5

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Blog